WHAT ARE OUR PRODUCTS MADE OF?
Alabastrite
Alabastrite is product line name for polyresin items. Alabastrite is a stone-based material which can be intricately molded producing great detail, and will allow paint to adhere. These items may be cleaned by dusting, however, they should not be washed with water as they are painted with water soluble paints.
Bone China
White clay with bone ash added. Bone ash content must be at least 25% by U. S. guidelines. Fired at 1800 degrees. The translucent material is finished with a glaze or underglaze (matte). Lighter, stronger, more expensive than porcelain.
Porcelain
Fine ground white clay, molded and fired in an oven for eight hours at 1200 degrees. Finished with a glazed, underglazed, or "bisque" finish. Glazing produces a high gloss; underglaze produces a matte finish. Bisque is a matte finish without glaze. After finishing, the item is "cooked" for six hours at 800 degrees.
Jade Porcelain
Jade porcelain is a type of porcelain made with a finer clay. Usually no glaze or only a colorless glaze will be applied at the final firing to show off the very smooth surface and to preserve the translucency. Example: 27112. Jade Porcelain is used for night lights because of its high degree of translucency when lit.
Stoneware
White clay with fine ground stone. Working with stoneware demands great expertise, and is in fact becoming a lost art. Stoneware is safe to use in microwave and conventional ovens.
Patchwork Items
Unique fabric or paper prints are applied to the surface of porcelain, dolomite or polyresin items. After application, 12 layers of lacquer are added and the item is hand polished to a high gloss between each layer.
Cubic Zircon
The most successful simulated diamond. Properties such as refraction, hardness, and specific gravity are remarkably similar to diamonds. Cubic zirconia are very hard to distinguish from diamonds; sometimes a jewelers loop will be needed to see the difference.
Diamond
Extremely hard, highly refractive colorless or white crystalline of carbon. Diamonds, like all gemstones, are judged in terms of Carats, or weight (different from Karats, as in gold purity).
Gold
The ultimate precious metal. Virtually indestructible, amazingly malleable, does not rust or tarnish. Graded by purity, in the U.S. a scale of 24 is used, so 24 Karats (24K) is 100% pure. 18K is 18 parts gold and 6 parts alloy (other metals), and so on. 10K is the legal minimum for Karat-graded gold. The word "Plumb" indicates the exact purity of the piece.
Gemstones
Rubies, sapphires, emeralds and amethysts, often treasured as birthstones, fall under the category of gemstones. (Birthstones are listed in the back of your WOP catalog.) Gemstones are priced and graded by Carat weight.
Pearl
A smooth, lustrous, variously-colored deposit formed around a grain of sand in the shell of a certain mollusk. Pearls may be formed naturally or "cultured" through an artificial implanting process.
Sterling Silver
To qualify as "sterling" a given piece must be composed of a least 92.5% pure silver.
Titanium
TITANIUM (Ti, atomic number 22) is a lustrous, grey metallic element used principally to make lightweight, resistant alloys. It is one of the transitional elements of the periodic table and has many desirable properties, most notably its incredible strength and durability.
Titanium is immune to corrosive attacks by saltwater and marine atmosphere, and exhibits exceptional resistance to a broad range of corrosive gases, acids and alkalis. Immune to microbiologically influenced corrosion, Titanium is physiologically inert and hypoallergenic.
Titanium is virtually non-magnetic, as well, making it ideal for applications where electromagnetic interference must be minimized.
Titanium exhibits a high strength to weight ratio. Pure titanium is stronger than steel yet nearly 50% lighter. When added to various alloys, its hardness, toughness and tensile strength can be increased dramatically.
Titanium is always found in combination with other substances, and occurs as an oxide in ilmenite, rutile and sphene, and is present in titanates and in many iron ores. Titanium is present in the ash of coal, in plants, and in the human body. Titanium is ductile only when it is free of oxygen and nitrogen (air), melting at 1660°C (3020°F) and boiling at 3287°C (5949°F).
The complex process of converting titanium ore into metal has been commercially viable for a little more than 50 years. Since the commercial introduction of titanium, its use has expanded by an average of 8% per year and its popularity continues to grow.
Hong Tze
To closely emulate a special stone found in China which is known for its deep red color, these items are created using an alabastrite polyresin. Hong Tze pieces are highly polished, further bringing out the intense, deep red color.
Frosted Acrylic
Acrylic items are given the French Lilac process, (used on glass), to achieve the distinctive frosted look. Example: 27205. The drama of frosted glass without the weight.
Gypsum
Gypsum is a white mineral which is usually used to make Plaster of Paris.
Dolomite
A magnesia-rich, sedimentary rock resembling limestone, dolomite is either gray, pink or white in color.
|
|
|
|
|
|